1K-2K SOLVENT BASED ACRYLIC SYSTEMS RESINS
THERMOPLASTIC&THERMO SETTING ACRYLIC RESIN
ATTACRYL A144
50% Solution in toluene/xylene, thermoplastic acrylic resin.
SYNTHALAT A060
1,8 OH Hydroxyl content, 60% in xylene, polyisocyanate-curing acrylic resin.
SYNTHALAT A077
2.6 OH Hydroxyl content, 60% in xylene , polyisocyanate-curing acrylic resin.
Mixing Ratio With Poly Isocyanates
Based on an equivalent reaction of the reactive groups (NCO : OH=1 : 1) the formula below calculates the quantity of polyisocyanate to be added, relative to 100 pts/wt solid SYNTHALAT A077
| 42 x 100 x 2.6 |
| 17 x NCO% |
| 42 | = | Molecular weight of NCO groups |
| 17 | = | Molecular weight of OH groups |
| 2.6 | = | %Hydroxyl content of SYNHALAT A077 relative to non-volatile content |
| 42 | = |
Molecular weight of NCO groups |
| 17 | = | Molecular weight of OH groups |
| 2.6 | = | %Hydroxyl content of SYNHALAT A077 relative to non-volatile content |
ATTACRYL A-HF 097
4.2 OH Hydroxyl content, 70% in butyl acetate. Polyisocyanate-curing acrylic resin.
Mixing Ratio With Poly-Isocyanates
Based on an equivalent reaction of the reactive groups (NCO : OH=1 : 1) the formula below calculates the quantity of polyisocyanate to be added, relative to 100 pts/wt solid ATTACRYL A-HF 097
| 42 x 100 x 4.2 |
| 17 x NCO% |
| 42 | = | NCO gruplarının moleküler ağırlığı |
| 17 | = | OH grubunun moleküler ağırlığı |
| 4.2 | = | Uçucu olmayan içeriğe göre ATTACRYL A-HF 097’nin % hidroksil içeriği |